Description
TACKSOL KR 30 is a solvent based PSA based on a well balanced mixture of rubbers and resins. Such special formulation provides excellent adhesion values and also a good cohesion.
Application
TACKSOL KR 30 can be applied on a wide range of substrates, such as fabrics, non-woven, paper, PET, PP, PE, PVC, etc.
This product is suggested when high cohesion, good tack, high peel adhesion and good heat resistance are required.
Technical Specifications
| Method of analysis | MU | Standard | |
|---|---|---|---|
| 1 | Total Solids | % | 31±1 |
| 3 | Brookfield Viscosity 25°C | mPa.s | 8000 - 180001 |
| Solvents | hexane / toluene | ||
| Notes | |||
| 1 | N. 5 RV; 20 RPM | ||
Film properties
| Method of analysis | MU | Standard | |
|---|---|---|---|
| 10 | Peel Adhesion on Steel | N/in | 18 |
| 22 | Static Shear | h | > 12 |
| 125 | Loop Tack | N | 10 |
| Average values; 22±2 g/m² of dry adhesive on PET film 36 µm | |||
Handling
TACKSOL KR 30 can be coated with rotating knife or knife-over-roll.
On plastic substrates a suitable primer is required (please see ICHEMCO catalogue).
To increase the heat or the mechanical resistance, 0.5-0.6% of CURING AGENT D should be added. In such case the adhesive pot-life of the adhesive is reduced to maximum 24 hours
Packaging
TACKSOL KR 30 is supplied in 200 l iron drums (about 150 Kg net).
Storing
Pruduct must be stored in a ventilated and dry place. Avoid flames presence.
Use within 12 months from production date (unopened and in the original packaging).
| Mod. DT3002E | Creation date: 7/15/2004 | Revision: 4 | Revision date: 6 Jun 2025 |
Above information is reliable, but does not constitute warranty.